Prof Henry Snaith FRS

Abstract:

The meteoric rise of the field of perovskite solar cells has been fueled by the ease with which a wide range of high-quality materials can be fabricated via simple solution processing methods. However, to date, little effort has been devoted to understanding the precursor solutions, and the role of additives such as hydrohalic acids upon film crystallization and final optoelectronic quality. Here, a direct link between the colloids concentration present in the [HC(NH2 )2 ]0.83 Cs0.17 Pb(Br0.2 I0.8 )3 precursor solution and the nucleation and growth stages of the thin film formation is established. Using dynamic light scattering analysis, the dissolution of colloids over a time span triggered by the addition of hydrohalic acids is monitored. These colloids appear to provide nucleation sites for the perovskite crystallization, which critically impacts morphology, crystal quality, and optoelectronic properties. Via 2D X-ray diffraction, highly ordered and textured crystals for films prepared from solutions with lower colloidal concentrations are observed. This increase in material quality allows for a reduction in microstrain along with a twofold increase in charge-carrier mobilities leading to values exceeding 20 cm2 V-1 s-1 . Using a solution with an optimized colloidal concentration, devices that reach current-voltage measured power conversion efficiency of 18.8% and stabilized efficiency of 17.9% are fabricated.

Abstract:

Metal halide perovskites such as methylammonium lead iodide (MAPbI3) are highly promising materials for photovoltaics. However, the relationship between the organic nature of the cation and the optoelectronic quality remains debated. In this work, we investigate the optoelectronic properties of fully inorganic vapour-deposited and spin-coated black-phase CsPbI3 thin films. Using the time-resolved microwave conductivity technique, we measure charge carrier mobilities up to 25 cm2/(V s) and impressively long charge carrier lifetimes exceeding 10 μs for vapour-deposited CsPbI3, while the carrier lifetime reaches less than 0.2 μs in the spin-coated samples. Finally, we show that these improved lifetimes result in enhanced device performance with power conversion efficiencies close to 9%. Altogether, these results suggest that the charge carrier mobility and recombination lifetime are mainly dictated by the inorganic framework rather than the organic nature of the cation.

Abstract:

During the past year, halide double perovskites attracted attention as potential lead-free alternatives to Pb-based halide perovskites. However, none of the compounds discovered so far can match the optoelectronic properties of MAPbI3 (MA = CH3NH3). Here we argue that, from the electronic structure viewpoint, the only option to make Pb-free double perovskites retaining the remarkable properties of MAPbI3 is to combine In and Bi as B(+) and B(3+) cations, respectively. While inorganic double perovskites such as Cs2InBiX6 were found to be unstable due to In(+) oxidizing into In(3+), we show that the +1 oxidation state of In becomes progressively more stable as the A-site cation changes from K to Cs. Hence, we propose the use of MA and FA [FA = CH(NH2)2] to stabilize A2InBiBr6 double perovskites. We show that the optoelectronic properties of A2InBiBr6 are remarkably similar to those of MAPbI3, and explore the mixed-cation (Cs/MA/FA)2InBiBr6 halide double perovskites.