Prof Henry Snaith FRS

Abstract:

Previous theoretical calculations show azetidinium has the right radial size to form a 3D perovskite with lead halides [1], and has been shown to impart, as the A-site cation of ABX3 unit, beneficial properties to ferroelectric perovskites [2]. However, there has been very limited research into its use as the cation in lead halide perovskites to date. In this communication we report the synthesis and characterization of azetidinium-based lead mixed halide perovskite colloidal nanocrystals. The mixed halide system is iodine and chlorine unlike other reported nanocrystals in the literature where the halide systems are either iodine/bromine or bromine/chlorine. UV-visible absorbance data, complemented with photoluminescence spectroscopy, reveals an indirect-bandgap of about 1.96 eV for our nanocrystals. Structural characterization using TEM shows two distinct interatomic distances (2.98 +/- 0.15 Angstroms and 3.43 +/- 0.16 Angstroms) and non-orthogonal lattice angles (approximately 112 degrees) intrinsic to the nanocrystals with a probable triclinic structure revealed by XRD. The presence of chlorine and iodine within the nanocrystals is confirmed by EDS spectroscopy. Finally, light-induced electron paramagnetic resonance (LEPR) spectroscopy with PCBM confirms the photoinduced charge transfer capabilities of the nanocrystals. The formation of such semiconducting lead mixed halide perovskite using azetidinium as the cation suggests a promising subclass of hybrid perovskites holding potential for optoelectronic applications such as in solar cells and photodetectors.

Abstract:

The production of highly efficient single‐ and multijunction metal halide perovskite (MHP) solar cells requires careful optimization of the optical and electrical properties of these devices. Here, precise control of CH3NH3PbI3 perovskite layers is demonstrated in solar cell devices through the use of dual source coevaporation. Light absorption and device performance are tracked for incorporated MHP films ranging from ≈67 nm to ≈1.4 µm thickness and transfer‐matrix optical modeling is utilized to quantify optical losses that arise from interference effects. Based on these results, a device with 19.2% steady‐state power conversion efficiency is achieved through incorporation of a perovskite film with near‐optimum predicted thickness (≈709 nm). Significantly, a clear signature of photon reabsorption is observed in perovskite films that have the same thickness (≈709 nm) as in the optimized device. Despite the positive effect of photon recycling associated with photon reabsorption, devices with thicker (>750 nm) MHP layers exhibit poor performance owing to competing nonradiative charge recombination in a “dead‐volume” of MHP. Overall, these findings demonstrate the need for fine control over MHP thickness to achieve the highest efficiency cells, and accurate consideration of photon reabsorption, optical interference, and charge transport properties.

Abstract:

The excellent optoelectronic properties demonstrated by hybrid organic/inorganic metal halide perovskites are all predicated on precisely controlling the exact nucleation and crystallization dynamics that occur during film formation. In general, high‐performance thin films are obtained by a method commonly called solvent engineering (or antisolvent quench) processing. The solvent engineering method removes excess solvent, but importantly leaves behind solvent that forms chemical adducts with the lead‐halide precursor salts. These adduct‐based precursor phases control nucleation and the growth of the polycrystalline domains. There has not yet been a comprehensive study comparing the various antisolvents used in different perovskite compositions containing cesium. In addition, there have been no reports of solvent engineering for high efficiency in all‐inorganic perovskites such as CsPbI3. In this work, inorganic perovskite composition CsPbI3 is specifically targeted and unique adducts formed between CsI and precursor solvents and antisolvents are found that have not been observed for other A‐site cation salts. These CsI adducts control nucleation more so than the PbI2–dimethyl sulfoxide (DMSO) adduct and demonstrate how the A‐site plays a significant role in crystallization. The use of methyl acetate (MeOAc) in this solvent engineering approach dictates crystallization through the formation of a CsI–MeOAc adduct and results in solar cells with a power conversion efficiency of 14.4%.

Abstract:

Mixed-halide perovskites are essential for use in all-perovskite or perovskite–silicon tandem solar cells due to their tunable bandgap. However, trap states and halide segregation currently present the two main challenges for efficient mixed-halide perovskite technologies. Here photoluminescence techniques are used to study trap states and halide segregation in full mixed-halide perovskite photovoltaic devices. This work identifies three distinct defect species in the perovskite material: a charged, mobile defect that traps charge-carriers in the perovskite, a charge-neutral defect that induces halide segregation, and a charged, mobile defect that screens the perovskite from external electric fields. These three defects are proposed to be MA+ interstitials, crystal distortions, and halide vacancies and/or interstitials, respectively. Finally, external quantum efficiency measurements show that photoexcited charge-carriers can be extracted from the iodide-rich low-bandgap regions of the phase-segregated perovskite formed under illumination, suggesting the existence of charge-carrier percolation pathways through grain boundaries where phase-segregation may occur.