Double perovskite crystals such as Cs₂AgBiBr₆ are expected to overcome the limitation of classic hybrid organic–inorganic perovskite crystals related to the presence of lead and the lack of structural stability. Perovskites are ionic crystals in which the carriers are expected to strongly couple to lattice vibrations. In this work we demonstrate that the photoluminescence (PL) emission in Cs₂AgBiBr₆ is strongly influenced by the strong electron–phonon coupling. Combining photoluminescence excitation (PLE) and Raman spectroscopy we show that the PL emission is related to a color center rather than a band-to-band transition. The broadening and the Stokes shift of the PL emission from Cs₂AgBiBr₆ is well explained using a Franck–Condon model with a Huang–Rhys factor of S = 11.7 indicating a strong electron–phonon interaction in this material.

Abstract:

Inorganic CsPbX3 (X = Cl, Br, I) perovskite nanocrystals (PNCs) are promising materials for next-generation optoelectronic applications due to their tunable emission and high color purity. However, there is still room to improve their photoluminescence quantum yields (PLQYs) in order to promote their applications. Herein, the PLQY of blue light emitting CsPb(Cl/Br)3 PNCs was increased to 83% with ammonium hexafluorophosphate by choosing an appropriate treatment time. The salt peeled off the outermost surface of PNCs with halide vacancies and then passivated the surface. This method is effective at improving the PLQYs of different CsPbX3 (X = Cl, Br, I) PNCs covering the entire visible spectrum; the PLQYs were improved to 25% for CsPbCl3 at 398 nm, 83% for CsPb(Cl/Br)3 at 448 nm, 96% for CsPbBr3 at 504 nm, 86% for CsPb(Br/I)3 at 568 nm, and 98% for CsPbI3 at 687 nm.