Prof Henry Snaith FRS

Abstract:

The power-conversion efficiency of perovskite solar cells has soared up to 22.1% earlier this year. Within merely five years, the perovskite solar cell can now compete on efficiency with inorganic thin-film technologies, making it the most promising of the new, emerging photovoltaic solar cell technologies. The next grand challenge is now the aspect of stability. The hydrophilicity and volatility of the organic methylammonium makes the work-horse material methylammonium lead iodide vulnerable to degradation through humidity and heat. Additionally, ultraviolet radiation and oxygen constitute stressors which can deteriorate the device performance. There are two fundamental strategies to increasing the device stability: developing protective layers around the vulnerable perovskite absorber and developing a more resilient perovskite absorber. The most important reports in literature are summarized and analyzed here, letting us conclude that any long-term stability, on par with that of inorganic thin-film technologies, is only possible with a more resilient perovskite incorporated in a highly protective device design.

Abstract:

Metal halide perovskites have emerged as one of the most promising materials for photovoltaics (PVs), with power conversion efficiency of over 22% already demonstrated. In order to compete with traditional crystalline silicon PV, cost and stability are equally important issues that need to be considered besides efficiency. Copper thiocyanate (CuSCN) is an interesting candidate to be used as an inexpensive, thermally stable p-type charge conducting material in perovskite solar cells. Here, we report 13% efficient perovskite solar cells employing CuSCN as the hole-transport material. We compare the stability of cells employing CuSCN with those employing the archetypical organic hole-transporter 2,2′,7,7′-Tetrakis (N,N-di-p-methoxyphenyl-amine) 9,9′-Spirobifluorene (Spiro-OMeTAD), under elevated temperature in ambient atmosphere. Surprisingly, we find that the devices employing CuSCN degrade faster under elevated temperatures than the devices employing Spiro-OMeTAD. We discover that an interfacial degradation mechanism occurs at the heterojunction between the perovskite absorber and the CuSCN, even in a dry nitrogen atmosphere, identifying the presence of a critical instability. Interestingly, with the additional coating of the completed cells with a thin film of insulating poly(methyl methacrylate) (PMMA), functioning as a rudimentary “on-cell” encapsulation, we significantly alleviate this issue and deliver efficient perovskite solar cells which survive for more than 1000 hours at 85 °C in air with only 25% degradation in performance. Beyond identifying a critical area to address in order to enable CuSCN to be useful for long term operation in perovskite solar cells, our findings indicate that the role of the “encapsulant” is to both keep the environment out, and keep degradation products within the cell.