Abstract:

We adopt a reverse Monte Carlo refinement approach, using experimental X-ray total scattering data, to develop a structure model for synthetic, hydrated amorphous calcium carbonate (ACC). The ACC is revealed to consist of a porous calcium-rich framework that supports interconnected channels containing water and carbonate molecules. The existence of a previously unrecognized nanometer-scale channel network suggests mechanisms of how additives can be accommodated within the structure and provide temporary stabilization, as well as influence the crystallization process. Moreover, while lacking long-range order, the calcium-rich framework in the ACC contains similar Ca packing density to that present in calcite, aragonite, and vaterite, yielding clues of how the amorphous material converts into the different crystalline forms. Our results provide a new starting point for advancing our understanding of biomineralization as well as the development of biomimetic approaches to next-generation materials synthesis. © 2010 American Chemical Society.

Abstract:

We have used inelastic neutron scattering and muon-spin rotation to compare the low energy magnetic excitations in single crystals of superconducting Fe(1.01)Se(0.50)Te(0.50) and non-superconducting Fe(1.10)Se(0.25)Te(0.75). We confirm the existence of a spin resonance in the superconducting phase of Fe(1.01)Se(0.50)Te(0.50), at an energy of 7 meV and a wavevector of (1/2, 1/2, 0). The non-superconducting sample exhibits two incommensurate magnetic excitations at (1/2, 1/2, 0) ± (0.18, - 0.18, 0) which rise steeply in energy, but no resonance is observed at low energies. A strongly dispersive low energy magnetic excitation is also observed in Fe(1.10)Se(0.25)Te(0.75) close to the commensurate antiferromagnetic ordering wavevector (1/2 - δ, 0, 1/2), where δ≈0.03. The magnetic correlations in both samples are found to be quasi-two-dimensional in character and persist well above the magnetic (Fe(1.10)Se(0.25)Te(0.75)) and superconducting (Fe(1.01)Se(0.50)Te(0.50)) transition temperatures.