Dr Ashley Marshall

Abstract:

We present the synthesis of formamidinium lead tribromide (FAPbBr3) perovskite nanocrystals through a phosphine oxide route, where in comparison to more traditional syntheses oleylamine is replaced with trioctylphosphine oxide (TOPO). This route has previously been shown to be successful for the inorganic cesium lead tribromide perovskite nanocrystals. We examine the interactions between the precursors via nuclear magnetic resonance spectroscopy (NMR). We confirm the existence of an interaction between FA-oleate and TOPO and use this to guide the optimization of our synthesis. When the reaction is conducted at room temperature, we observe the formation of nanoparticles with high photoluminescence quantum yield (PLQY, ∼70%) at 2.39 eV (518 nm) with little ripening or size defocusing over time. Although we obtain narrow emission peaks, the crystals are irregular in shape—a testament to the impact of the FA-oleate:TOPO interaction. Despite a drop in PLQY in the washed solutions, films made maintain a high PLQY of ∼50% at 2.33 eV (532 nm), which is fortuitously the ideal wavelength for the green emission channel in displays, and we demonstrate 532 nm electroluminescence in light-emitting diodes with an EQE of 3.7%.

Abstract:

We show nanoscale phase stabilization of CsPbI3 quantum dots (QDs) to low temperatures that can be used as the active component of efficient optoelectronic devices. CsPbI3 is an all-inorganic analog to the hybrid organic cation halide perovskites, but the cubic phase of bulk CsPbI3 (α-CsPbI3)-the variant with desirable band gap-is only stable at high temperatures. We describe the formation of α-CsPbI3 QD films that are phase-stable for months in ambient air. The films exhibit long-range electronic transport and were used to fabricate colloidal perovskite QD photovoltaic cells with an open-circuit voltage of 1.23 volts and efficiency of 10.77%. These devices also function as light-emitting diodes with low turn-on voltage and tunable emission.

Abstract:

The excellent optoelectronic properties demonstrated by hybrid organic/inorganic metal halide perovskites are all predicated on precisely controlling the exact nucleation and crystallization dynamics that occur during film formation. In general, high‐performance thin films are obtained by a method commonly called solvent engineering (or antisolvent quench) processing. The solvent engineering method removes excess solvent, but importantly leaves behind solvent that forms chemical adducts with the lead‐halide precursor salts. These adduct‐based precursor phases control nucleation and the growth of the polycrystalline domains. There has not yet been a comprehensive study comparing the various antisolvents used in different perovskite compositions containing cesium. In addition, there have been no reports of solvent engineering for high efficiency in all‐inorganic perovskites such as CsPbI3. In this work, inorganic perovskite composition CsPbI3 is specifically targeted and unique adducts formed between CsI and precursor solvents and antisolvents are found that have not been observed for other A‐site cation salts. These CsI adducts control nucleation more so than the PbI2–dimethyl sulfoxide (DMSO) adduct and demonstrate how the A‐site plays a significant role in crystallization. The use of methyl acetate (MeOAc) in this solvent engineering approach dictates crystallization through the formation of a CsI–MeOAc adduct and results in solar cells with a power conversion efficiency of 14.4%.

Abstract:

Light-emitting diodes (LEDs) made from metal halide perovskites have demonstrated external electroluminescent quantum efficiencies (EQEEL) in excess of 20%. However, their poor operational stability, resulting in lifetimes of only tens to hundreds of hours, needs to be dramatically improved prior to commercial use. There is little consensus in the community upon which factors limit the stability of these devices. Here, we investigate the role played by ammonium cations on the operational stability. We vary the amount of phenylethylammonium bromide, a widely used alkylammonium salt, that we add to a precursor solution of CsPbBr3 and track changes in stability and EQEEL. We find that while phenylethylammonium bromide is beneficial in achieving high efficiency, it is highly detrimental to operational stability. We investigate material properties and electronic characteristics before and after degradation and find that both a reduction in the radiative efficiency of the emitter and significant changes in current–voltage characteristics explain the orders of magnitude drop in the EQEEL, which we attribute to increased ionic mobility. Our results suggest that engineering new contacts and further investigation into materials with lower ionic mobility should yield much improved stability of perovskite LEDs.