Advanced Functional Materials and Devices (AFMD) Group

Abstract:

Formamidinium lead triiodide (FAPbI₃) is the leading candidate for single-junction metal–halide perovskite photovoltaics, despite the metastability of this phase. To enhance its ambient-phase stability and produce world-record photovoltaic efficiencies, methylenediammonium dichloride (MDACl₂) has been used as an additive in FAPbI₃. MDA²⁺ has been reported as incorporated into the perovskite lattice alongside Cl^–. However, the precise function and role of MDA²⁺ remain uncertain. Here, we grow FAPbI₃ single crystals from a solution containing MDACl₂ (FAPbI₃-M). We demonstrate that FAPbI₃-M crystals are stable against transformation to the photoinactive δ-phase for more than one year under ambient conditions. Critically, we reveal that MDA²⁺ is not the direct cause of the enhanced material stability. Instead, MDA²⁺ degrades rapidly to produce ammonium and methaniminium, which subsequently oligomerizes to yield hexamethylenetetramine (HMTA). FAPbI₃ crystals grown from a solution containing HMTA (FAPbI₃-H) replicate the enhanced α-phase stability of FAPbI₃-M. However, we further determine that HMTA is unstable in the perovskite precursor solution, where reaction with FA⁺ is possible, leading instead to the formation of tetrahydrotriazinium (THTZ-H⁺). By a combination of liquid- and solid-state NMR techniques, we show that THTZ-H⁺ is selectively incorporated into the bulk of both FAPbI₃-M and FAPbI₃-H at ∼0.5 mol % and infer that this addition is responsible for the improved α-phase stability.

Abstract:

In this work, we couple theoretical and experimental approaches to understand and reduce the losses of wide bandgap Br-rich perovskite pin devices at open-circuit voltage (V_OC) and short-circuit current (J_SC) conditions. A mismatch between the internal quasi-Fermi level splitting (QFLS) and the external V_OC is detrimental for these devices. We demonstrate that modifying the perovskite top-surface with guanidinium-Br and imidazolium-Br forms a low-dimensional perovskite phase at the n-interface, suppressing the QFLS-V_OC mismatch, and boosting the V_OC. Concurrently, the use of an ionic interlayer or a self-assembled monolayer at the p-interface reduces the inferred field screening induced by mobile ions at J_SC, promoting charge extraction and raising the J_SC. The combination of the n- and p-type optimizations allows us to approach the thermodynamic potential of the perovskite absorber layer, resulting in 1 cm² devices with performance parameters of V_OCs up to 1.29 V, fill factors above 80% and J_SCs up to 17 mA/cm², in addition to a thermal stability T₈₀ lifetime of more than 3500 h at 85 °C.

Abstract:

All data used in the publication are deposited both as Origin Pro and csv files.

Abstract:

Vacuum deposition is a solvent-free method suitable for growing thin films of metal halide perovskite (MHP) semiconductors. However, most reports of high-efficiency solar cells based on such vacuum-deposited MHP films incorporate solution-processed hole transport layers (HTLs), thereby complicating prospects of industrial upscaling and potentially affecting the overall device stability. In this work, we investigate organometallic copper phthalocyanine (CuPc) and zinc phthalocyanine (ZnPc) as alternative, low-cost, and durable HTLs in all-vacuum-deposited solvent-free formamidinium-cesium lead triodide [CH(NH₂)₂]_0.83Cs_0.17PbI₃ (FACsPbI₃) perovskite solar cells. We elucidate that the CuPc HTL, when employed in an “inverted” p–i–n solar cell configuration, attains a solar-to-electrical power conversion efficiency of up to 13.9%. Importantly, unencapsulated devices as large as 1 cm² exhibited excellent long-term stability, demonstrating no observable degradation in efficiency after more than 5000 h in storage and 3700 h under 85 °C thermal stressing in N₂ atmosphere.