Quantum matter in high magnetic fields

Abstract:

We report structural, magnetic, and magnetotransport properties of the two-dimensional chromium sulfide Cr2S2.92, which contains both Cr3+ and Cr2+ ions. Below its magnetic-ordering temperature (TN=118 K), Cr2S2.92 exhibits a weak spontaneous magnetization with a maximum around 90 K and a value of 0.013(4) μB per Cr ion at 5 K. The resistivity and magnetoresistance exhibit pronounced local maxima around TN (MR=48% in a field of 14 T). The magnetotransport properties are discussed in terms of magnetic-polaron formation.

Abstract:

It is shown by magnetometry and microSR spectroscopy that short-range magnetic interactions between the Mn cations in the nonmetallic K(2)NiF(4)-like phase La(0.8)Sr(1.2)Mn(0.6)Rh(0.4)O(4) become significant below approximately 200 K. Negative magnetoresistance (rho/rho(0) approximately 0.5 in 14 T at 108 K) is apparent below this temperature. Neutron diffraction has shown that an applied magnetic field of 5 T is sufficient to induce saturated (3.38(7)mu(B) per Mn) long-range ferromagnetic ordering of the atomic moments at 2 K, and that the induced ordering persists up to a temperature of 50 K in 5 T. Spin glass behavior is observed below 20 K in the absence of an applied field. The induced magnetic ordering is attributed to the subtle changes in band structure brought about by the external field, and to the controlling influence of Rh(3+) over the relative strength of competing magnetic exchange interactions.

Abstract:

A series of novel double perovskites La1+xA1-xInMnO6-δ (A = Sr, Ba) has been prepared and the room temperature crystal structures have been refined using X-ray and neutron powder diffraction. In all cases the B-site is occupied by a disordered arrangement of In3+ and Mn3+/4+ cations. However, whereas La1+xBa1-xInMnO6-δ exhibits two octahedral tilts and exists in a body-centred cell, space group Imma, La1+xSr1-xInMnO6-δ adopts the three-tilt GdFeO3 structure and has a primitive orthorhombic structure, space group Pnma. Magnetic susceptibility data show that all the compositions synthesised exhibit a spin glass freezing transition at ∼8 K. A negative magnetoresistance Δρ/ρ0 = 10.5% was measured at 164 K in a field of 14 T.

Abstract:

The substitution of Ga(3+) into the Jahn--Teller distorted, antiferromagnetic perovskites LaMnO(3) and NdMnO(3) strongly affects both the crystal structures and resulting magnetic ordering. In both compounds the Ga(3+) and Mn(3+) cations are disordered over the six coordinate sites. La(2)GaMnO(6) is a ferromagnetic insulator (T(c) = 70 K); a moment per Mn cation of 2.08(5) mu(B) has been determined by neutron powder diffraction at 5 K. Bond length and displacement parameter data suggest Jahn--Teller distortions which are both coherent and incoherent with the Pnma space group symmetry of the perovskite structure (a = 5.51122(4) A, b = 7.80515(6) A, c = 5.52947(4) A) at room temperature. The coherent distortion is strongly suppressed in comparison with the parent LaMnO(3) phase, but the displacement ellipsoids suggest that incoherent distortions are significant and arise from local Jahn--Teller distortions. The preparation of the new phase Nd(2)GaMnO(6) has been found to depend on sample cooling rates, with detailed characterization necessary to ensure phase separation has been avoided. This compound also adopts the GdFeO(3)-type orthorhombically distorted perovskite structure (space group Pnma, a = 5.64876(1) A, b = 7.65212(2) A, c = 5.41943(1) A at room temperature). However, the B site substitution has a totally different effect on the Jahn--Teller distortion at the Mn(3+) centers. This phase exhibits a Q(2) mode Jahn--Teller distortion similar to that observed in LaMnO(3), although reduced in magnitude as a result of the introduction of Ga(3+) onto the B site. There is no evidence of a dynamic Jahn-Teller distortion. At 5 K a ferromagnetically ordered Nd(3+) moment of 1.06(6) mu(B) is aligned along the y-axis and a moment of 2.8(1) mu(B) per Mn(3+) is ordered in the xy plane making an angle of 29(2) degrees with the y-axis. The Mn(3+) moments couple ferromagnetically in the xz plane. However, along the y-axis the moments couple ferromagnetically while the x components are coupled antiferromagnetically. This results in a canted antiferromagnetic arrangement in which the dominant exchange is ferromagnetic. Nd(2)GaMnO(6) is paramagnetic above 40(5) K, with a paramagnetic moment and Weiss constant of 6.70(2) mu(B) and 45.9(4) K, respectively. An ordered moment of 6.08(3) mu(B) per Nd(2)GaMnO(6) formula unit was measured by magnetometry at 5 K in an applied magnetic field of 5 T.